Extrusion: How Hopper Crammers Can Help Feeding

A crammer can assist the flow of certain polymers into the extruder. But the design is not universal and very material dependent. Here’s what you need to know.

Share

There are some polymers that are not free-flowing enough for conventional hopper-fed extruders even with optimal feed-throat and hopper designs. Then there are materials that have such a low bulk density that they significantly reduce the output of the extruder. And some materials have both issues. One solution is to add a hopper crammer.

Although it looks like a relatively simple device, designing a hopper crammer requires a tricky combination of experience and engineering. There is no universal crammer design; it depends heavily on the characteristics of the material being crammed. So it’s important to understand the polymer particles’ characteristics for flow, packing, bridging, and bulk density to determine how to design the crammer. Most of this analysis is done using small material samples along with reviewing the current feeding performance of the extruder.

The goal of a properly designed crammer is to deliver material to the extruder screw uniformly without generating much temperature rise or excessive pressure.

The free-flowing characteristics can usually be estimated by the angle of repose and by passing the material through a large funnel. Packing can be estimated by putting a cup-full into a plastic bag and squeezing it. Bridging is related to both the angle of repose and the packing. Bulk density can be measured by simply filling a calibrated container and weighing it. With that data you can size the hopper for adequate capacity to service the extruder’s desired output and start to develop the crammer design.

To design the auger there are helpful tables of tubular screw-conveyor data on the internet that take into account similar material characteristics. But they do not provide for compaction of very low-bulk-density materials. That is always an unknown and is based almost entirely on experience. Kase Conveyors has a handy screw guide on its website that I have found useful. It estimates the screw speed and horsepower needed How Hopper Crammers Can Help Feeding to feed some materials, allowing you to specify the auger and drive system. Naturally some margin for error must be allowed, as there are no exact formulas and no exact measurements of the materials’ characteristics. Since the auger is operating vertically downward, the rate typically meets or exceeds the rates noted for tubular screw conveyors that are based on no elevation change.

Most crammer augers use a standard flight pitch, as that usually provides the best overall results, unless there is actual data available on other helix angles for that particular material. Figure 1 is typical of a crammer for a poorly flowing but higher bulk-density material, where bridging or tunneling of the material is problematic. Figure 2 is typical of a crammer for low-bulk-density materials like film or foam. The difference is that the auger in Fig. 2 tapers outward to conform to the hopper taper. This lets it get a bigger “bite” of the low-bulk-density material and give it some preliminary compaction as it enters the auger.

The crammer hopper must be of much heavier construction than a conventional hopper because it has to resist the torque of the screw rotation as well as the upward thrust of the screw. A 6-in. crammer auger that generates only 200 psi of polymer pressure will generate more 5500 lb of upward thrust force. Consequently, you’ll need a thrust bearing with radial bearings for alignment to isolate the reducer/motor from the thrust and support the screw shaft—just like a thrust assembly on an extruder.

Get more insights on Extrusion from our expert authors: Extrusion Know How

The hopper cover or lid also must be very strong to resist bending from the upward screw thrust and to support the weight of the reducer/drive. At the entrance to the feed throat, a hardened or bimetallic bushing is usually used to reduce wear from the auger rotation because it has little centering support due to the long shaft and has extra clearance to prevent frictional melt formation. As a result, it sort of “bangs around” in the bushing, causing wear. The bushing should be in a water-cooled jacket to further prevent any melt from forming between the barrel wall and the screw flights, even with the added clearance. Any melt formation on the screw will completely stop the feeding and is difficult to clean—usually the entire crammer must be completely disassembled.

In addition to estimating the torque required for screw rotation, there is added torque required for rotation of the agitator arms. This is truly a guess based on the cross section of the agitator bars and the material characteristics. The angle of repose and the packing tendency govern that estimate. For the agitator bars to move through the material and prevent bridging, the material must not slip excessively on the hopper wall. That often requires bars to be mounted on the inner hopper wall to resist rotation of the entire mass in the hopper, just like in a grooved-barrel extruder.

The crammer hopper must be of much heavier construction than a conventional hopper because it has to resist the torque of the screw rotation as well as the upward thrust of the screw.

The goal of a properly designed crammer is to deliver material to the extruder screw uniformly without generating much temperature rise or excessive pressure. Over-cramming can bring on a lot of unintended consequences. Even with a very well-designed crammer and extruder screw there is a tendency for operators to over-drive it to boost output above the screw’s optimal rate. An over-driven crammer can cause surging as it “over-stuffs” the feed section, leading to inconsistent output, high screw/barrel wear, drive overload, poor melt quality, feed-throat melting, and even extruder reducer bearing failure due to a high side load on the bearings. Designs for low-bulk-density materials are generally more problematic than those for materials with poor flow.

Some extrusion operations cannot process effectively without use of a crammer or other device to assist polymer flow into the extruder. However, there are enough negative aspects to using a crammer that it’s advisable to be certain that changes in hopper, feed-throat, and screw design cannot solve the feeding issues before installing a crammer.


ABOUT THE AUTHOR: Jim Frankland is a mechanical engineer who has been involved in all types of extrusion processing for more than 40 years. He is now president of Frankland Plastics Consulting, LLC. Contact jim.frankland@comcast.net or (724) 651-9196.

Related Content

Understanding Strain-Rate Sensitivity In Polymers

Material behavior is fundamentally determined by the equivalence of time and temperature. But that principle tends to be lost on processors and designers. Here’s some guidance.

Read More
best practices

Why (and What) You Need to Dry

Other than polyolefins, almost every other polymer exhibits some level of polarity and therefore can absorb a certain amount of moisture from the atmosphere. Here’s a look at some of these materials, and what needs to be done to dry them.

Read More
Commodity Resins

Density & Molecular Weight in Polyethylene

This so-called 'commodity' material is actually quite complex, making selecting the right type a challenge.

Read More

A Simpler Way to Calculate Shot Size vs. Barrel Capacity

Let’s take another look at this seemingly dull but oh-so-crucial topic.

Read More

Read Next

Extrusion

Troubleshooting Screw and Barrel Wear in Extrusion

Extruder screws and barrels will wear over time. If you are seeing a  reduction in specific rate and higher discharge temperatures, wear is the likely culprit.   

Read More
close up on technology

Processor Turns to AI to Help Keep Machines Humming

At captive processor McConkey, a new generation of artificial intelligence models, highlighted by ChatGPT, is helping it wade through the shortage of skilled labor and keep its production lines churning out good parts.

Read More